『Abstract
In situ atomic force microscopy (AFM) was used to follow the
far-from-equilibrium dissolution of the {001} cleavage surface
of natural gibbsite in nitric acid. The main dissolution mechanism
was the retreat of straight monolayer steps, the edges of which
are parallel to the <110>, <010>, and <100>
directions. The stability of these steps can be expressed as <110>><010>><100>.
The results are explained in terms of the positions of the terminal
O atoms and their associated Al atoms at the steps. New steps
were formed at etch pits that opened where screw dislocations
emerged on the surface. The dissolution rates were calculated
from the change in size of pits and islands. The values obtained
were 9.5×10-9−2.3×10-8mol/m2・s,
normalized to the total surface area, and 1.8−3.6×10-7mol/m2・s,
normalized to the surface area of the step fronts. The rates of
dissolution calculated using only the surface area of the step
fronts are similar to literature values obtained by other methods.』
『現位置原子間力顕微鏡（AFM）が、硝酸中の天然ギブス石の｛001｝劈開面の平衡から離れた溶解をたどるために用いられた。主要な溶解メカニズムは、その稜が<110>、 <010>、および <100>方向に平行であるような、まっすぐな単層ステップの後退であった。これらのステップの安定性は<110>＞<010>＞<100>として表わすことができる。この結果は、ステップにおける終端O原子とそれらに伴うAl原子の配置の点から説明される。新しいステップは、螺旋転位が表面で発生した場所で開口したエッチピットにおいて形成された。溶解速度はピットと島の大きさの変化から計算された。得られた値は、全表面積にノーマライズすると9.5×10-9〜2.3×10-8モル/m2/秒で、ステップの前面の表面積にノーマライズすると1.8〜3.6×10-7モル/m2/秒であった。ステップ前面の表面積だけを用いて計算した溶解速度は、他の方法により得られた文献値と類似している。』