Casey et al.(1991)による〔『Dissolution rates of plagioclase at pH = 2 and 3』(211p)から〕

『pH2およびpH3 における斜長石の溶解速度』

【バッチ型の反応器による斜長石の溶解実験】
【斜長石の化学組成と溶解速度の関係】


Abstract
 The dissolution rates of plagioclase in acids are very sensitive to the mineral composition. At pH = 2.0 and 25゜C, rates range from ≒ 1 × 10-15 feldspar-mol/cm2/s for albite to greater than 1 × 10-12 feldspar-mol/cm2/s for anorthite. At pH = 3.0, the respective rates range from ≒ 3 × 10-16 feldspar-mol/cm2/s to ≒ 7 × 10-14 feldspar-mol/cm2/s. The relationship between mineral composition and dissolution rate, however, is not simple. In order to better define such a relation at pH = 2, rates were measured on eight plagioclase minerals and compared to existing data.
 In general, the dissolution rates of a given plagioclase mineral estimated by different researchers generally agree to within a factor of two to five. The uncertainty is much larger for Ca-rich minerals such as bytownite and anorthite, and reasons for the disagreement and unclear. Even with this uncertainty, however, it is apparent that dissolution rates vary nonlinearly with composition and that the rates for the Ca-rich minerals vary more with composition than Na-rich minerals.』

要旨
 斜長石の酸に対する溶解速度は、その鉱物組成にとても敏感である。pH2および25℃で、アルバイト(曹長石)に対する 1 × 10-15 長石モル/cm2/秒から、アノーサイト(灰長石)に対する 1 × 10-12 長石モル/cm2/秒以上までにわたる。pH3.0では、 3 × 10-16 長石モル/cm2/秒から 7 × 10-14 長石モル/cm2/秒の範囲である。しかし、鉱物組成と溶解速度の関係は単純ではない。pH2で、このような関係をもっと明らかにするために、8種類の斜長石試料について調べ、従来のデータと比較した。
 一般に、異なる研究者によって見積もられた、ある斜長石の溶解速度は2〜5倍の範囲内で一致する。バイトゥナイトおよびアノーサイトのようにCaに富むものは不確かさが非常に大きくなるが、その理由ははっきりしない。しかしこのような不確かさのある結果でさえ、溶解速度が組成に対して直線的には変動せず、Naに富むものよりCaに富むものの方が速度の変動が大きいことは明らかである。』

Introduction
Materials and techniques
 
Preparation of samples
 Feldspar compositions and sample purity
 Specific surface areas
 Dissolution experiments
Results
Discussion
Acknowledgments
References cited



戻る